High Speed Tool Steels

High Speed Tool Steels
High Speed Tool Steels
Product Code : 27
Product Description

Banking upon in-depth domain knowledge and years of vast experience, we are engaged in supplying High Speed Tool Steels. This kind steel is suitable for conditions involving thermal stresses and discontinuous cutting. Also, these steels are used in gear cutter, highly stressed twist drills and taps, profile knives, machining of high-strength material and broaches. Clients can avail our steel in different sizes and specifications as per their requirements. We offer these High Speed Tool Steels at cost effective prices to clients. 

Features:

  • Sturdy and durable
  • Light weight
  • Corrosion proof

High Speed Steel M-35 (Din-1.3243)

Steel Properties : This kind steel is suitable for conditions involving thermal stresses and discontinuous cutting. Heavy-duty miling cutters of all kinds, gear cutter, highly stressed twist drills and taps, profile knives, machining of high-strength material, broaches.

Applications : It is one of the W-Mo Co hss grade with good cutting character. The res hardness, hot hardness and wearing resistance are all better than W6M05Cr4V2.


Similar steel grade

BRAZIL

AUSTRIA

GERMANY

SLOVANIA

JAPAN

CHEZ. REP

VILLARES

BOHLER

DEW

RAVNE

HITACHI

NIPPON

RAVNE

VK5E
S700
1.3245
BRCMO
YXM4
HM35
MAXSP 75D

Chemical Composition: (%) 

Indian
Chemical Analysis Typical Value % (Min - Max)
Delivery Condition
IS
C
S
P
Si
Mn
Cr
Mo
V
W
Co
 
Heat
Treatment
Hardness
X190W6Co
M05Cr4V2
0.88-
0.96
<0.03
<0.03
0.20-
0.45
0.20-
0.40
3.80-
4.50
4.70-
0.52
1.70-
2.00
6.00-
6.70
4.55-
5.50
 
Annealed
<255


Production process:

EAF→LF→VD→ESR→BLOOM IN FOLLOWING MACHINE :
QUICK FORGING (12.5MN), HAMMER, PRECISION FORGING
 Precision forging : ï¿ 81-255mm
→Hot Rolled & Peeled : ¢14.5-80.0mm
 Hot Rolled : ï¿ 5.0-16.0mm (Coil) --->Cold Ground/Drawn: ï¿ 2.2-14.4MM


UNDER ANNEALED CONDITION :REDUCTION RATIO :DELIVERY STATUS :
Hardness : HB205-255As 1:4 or 1:5As Cold drawn / Hot rolled / forged, in annealed condition.


Size : Rounds

Cold Drawn/Ground Bar
Hot Rolled Annealed & Peeled Bar
Forged + Annealed + Turned Bar
Coil
ï¿ 2.2 - 14.4mm
ï¿ 14.5 - 80.0mm
ï¿ 81.0 - 255.0mm
ï¿ 5.0 - 16.0mm

Size : Hot Rolled Flat Bars / Sand Blasted & Machined Straight

Thickness
Width
12mm - 80mm
105mm - 305mm
SIZE : SQUARES
7.2mm - 27mm
SIZE : SHEET
1.2mm - 8mm

Heat Treatment :

Annealing:
Annealing temperature:860-880℃, keep this temperature by 2-4 hours, then cooling to 600℃ in the speed of less than 30℃/h.
if after cold drawn process, suggest and stress relieving annealing process Under the temperature of 600-700℃, keep this temperature
by 2 houres.
Quenching & Tempering (saltbath)

Quenching:
Pre-heating in two steps:
Heating temperature under: 400-500℃ and 850-900℃
Austenitizing temperature: 1180-1220℃
Heating coefficient 10-15sec/mm, quenching under 580-620℃, then cooling to room temperature.

Tempering:
Tempering temperature under: 540-560℃, tempering 3 times, each time 1 hour, then cooling to room temperature.

 